Type | Agressive media |
Non-aggressive media |
Max. temperature P-Flange |
Max. temperature V-Flange |
Max. temperature PFH-100 |
Min. temperature | Max. pressure | Min. pressure | Axial flexibility |
Lateral flexibility |
---|---|---|---|---|---|---|---|---|---|---|
Butyl 600GS | Wet | Wet | 80 °C (176 °F) |
80 °C (176 °F) |
180 °C (356 °F) |
-35 °C (-31 °F) |
0.35 bar (5 PSI) |
-0.35 bar (-5 PSI) |
25 % | 13 % |
EPDM 400G | Wet | Wet | 120 °C (248 °F) |
120 °C (248 °F) |
220 °C (428 °F) |
-35 °C (-31 °F) |
0.35 bar (5 PSI) |
-0.35 bar (-5 PSI) |
35 % | 18 % |
EPDM 600GG | Wet | Wet | 120 °C (248 °F) |
120 °C (248 °F) |
220 °C (428 °F) |
-35 °C (-31 °F) |
0.35 bar (5 PSI) |
-0.35 bar (-5 PSI) |
25 % | 13 % |
EPDM 600S | Wet | Wet | 120 °C (248 °F) |
120 °C (248 °F) |
220 °C (428 °F) |
-35 °C (-31 °F) |
0.35 bar (5 PSI) |
-0.35 bar (-5 PSI) |
25 % | 13 % |
FKM 320G | Wet | Wet | 200 °C (392 °F) |
200 °C (392 °F) |
300 °C (572 °F) |
-25 °C (-13 °F) |
0.2 bar (2.9 PSI) |
-0.2 bar (-2.9 PSI) |
35 % | 18 % |
FKM 350S | Wet | Wet | 200 °C (392 °F) |
200 °C (392 °F) |
300 °C (572 °F) |
-25 °C (-13 °F) |
0.35 bar (5 PSI) |
-0.35 bar (-5 PSI) |
25 % | 18 % |
FKM 450GS | Wet | Wet | 200 °C (392 °F) |
200 °C (392 °F) |
300 °C (572 °F) |
-25 °C (-13 °F) |
0.35 bar (5 PSI) |
-0.35 bar (-5 PSI) |
30 % | 15 % |
FKM 600GG | Wet | Wet | 200 °C (392 °F) |
200 °C (392 °F) |
300 °C (572 °F) |
-25 °C (-13 °F) |
0.35 bar (5 PSI) |
-0.35 bar (-5 PSI) |
25 % | 13 % |
FKM 600GS | Wet | Wet | 200 °C (392 °F) |
200 °C (392 °F) |
300 °C (572 °F) |
-25 °C (-13 °F) |
0.35 bar (5 PSI) |
-0.35 bar (-5 PSI) |
25 % | 13 % |
C | Wet | Wet | 270 °C (518 °F) |
270 °C (518 °F) |
400 °C (752 °F) |
-35 °C (-31 °F) |
0.2 bar (2.9 PSI) |
-0.2 bar (-2.9 PSI) |
50 % | 20 % |
O | Wet | Wet | 270 °C (518 °F) |
270 °C (518 °F) |
400 °C (752 °F) |
-35 °C (-31 °F) |
0.2 bar (2.9 PSI) |
-0.2 bar (-2.9 PSI) |
50 % | 20 % |
HD | Wet | Wet | 300 °C (572 °F) |
300 °C (572 °F) |
425 °C (797 °F) |
-35 °C (-31 °F) |
0.2 bar (2.9 PSI) |
-0.2 bar (-2.9 PSI) |
50 % | 20 % |